MgF2 (Magnesium Fluoried) is ‘n robuuste, harde en positiewe birefringent kristal wat bestand is teen termiese en meganiese skok. MgF2 (Magnesium Fluoried) is deursigtig oor ‘n baie wye verskeidenheid golflengtes. Vensters, lense en prisma’s van hierdie materiaal kan oor die hele reeks golflengtes gebruik word van 0.11μm tot 7.5μm. Hoë kwaliteit sintetiese VUV grade MgF2 (Magnesium Fluoried) is redelik duur. Laaggraad MgF2 word soms in die infrarooi gebruik, maar dit is minderwaardig as CaF2 (Kalsium Fluoried). MgF2 (Magnesium Fluoried) is taai en werk en poets goed, maar dit is effens tweevoudig en moet gesny word met die optiese as loodreg op die vlak van die venster of lens.
Hono Optics bied ook HP (warmdruk) polikristalliese hoë doeltreffendheid dunfilm multilayer MgF2-optika wat by 7-9um funksioneer, wat hoofsaaklik as ‘n middel-infrarooi golfruitmateriaal gebruik word. Dit word gebruik om middel-infrarooi golfvektorkoepel te produseer. Met hoë infrarooi transmittansie, klein termiese uitbreidingskoëffisiënt, goeie meganiese eienskappe en lae voorbereidingskoste, is dit die beste materiaal vir middel-infrarooi golfvektorkoepel. Op die oomblik bied Honor koepel minder as Dia. 270mm x 85mm x 10mm, en Plate minder as Dia.360mm x 15mm. Honor Optics is die professionele VGV, UV en IR graad MgF2 optiese vervaardiger, welkom om die prys van groothandel MgF2 optika te raadpleeg. Welkom almal om groot grootte laser graad MgF2 optika te koop.
MgF2 (Magnesium Fluoried) het goeie meganiese eienskappe, chemiese stabiliteit, impakweerstand, groot anti-termiese skommelinge en straling. Dit is ook 'n positiewe birefringent kristal met hoë optiese transmissie vanaf die ultraviolet ultraviolet 0.11um na die infrarooi spektrum 7.5um, geskik vir optiese lense, wig- en venstervervaardiging. MgF2 word ook beskou as duursame materiaal in diep UV- en LWIR-toediening
hoë doeltreffendheid dun-film multilayer MgF2 optika is soortgelyk aan Kalsium Fluoried in sy weerstand teen water. Die MgF2 vensters is sensitief vir termiese skok, maar gaan nie weg nie. Bestraling lei nie tot kleursentrums nie.
MgF2 dubbelafwyking moet in ag geneem word voor die keuse van hierdie materiaal in optiese ontwerp. Dit is bestand teen termiese en meganiese skok. Dit is twee keer so moeilik as CaF2, maar net die helfte so hard soos Ge. Dit is aansienlik duurder as CaF2 en BaF2, maar gewoonlik nie duurder as LiF nie. MgF2 is diamant draaibaar.
Produkte vervaardig: Lense, Asferiese lense, Windows, Optiese Beamsplitters, Optiese Filters, Wedges, Prismas.
Oppervlakte-afwerking: Pools van 10-5, of 20-10 krasgraf word onderskeidelik teen ekstra koste behaal, hoofsaaklik vir UV-toepassings. Tipiese spesifikasies vir oppervlakkwaliteit in die sigbare en naby infrarooi streke is 'n 40-20 en 60-40 krasgraf in die 3 tot die 7μm-reeks.
Oppervlakte figuur: In die UV en Sigbare spektrale streke wissel die oppervlak figuur van 1/10 golf na 1/2 golf @ 0.6328μm. In die infrarooi, tipies benodigde oppervlak figuur wissel van 1/2 golf na 2 golwe @ 0.6328μm en is gespesifiseer afhangende van die stelsel prestasie vereistes.
AR coating opsies: Magnesium Fluoried kan AR bedek word vir gebruik in die infrarooi, maar oor die algemeen sonder veel verbetering in transmissie as gevolg van sy lae brekingsindeks en alreeds hoë transmissie.
| Optical Properties | |
| Transmission Range | 110 nm to 7.5 μm |
| Transmittance | >90% at 193 nm to 6 μm |
| Refractive Index | No=1.37608; Ne=1.38771 (at 0.7μm) |
| Reflection Loss | 5.2% at 0.6 μm (both surfaces) |
| Residual Radiation Peak | 20 nm |
| Absorption Coefficient | 0.04 cm-1 at 2.7 μm |
| dn/dT | 2.3 x 10-6 /℃ parallel c-axis
1.7 x 10-6 /℃ perpendicular c-axis |
| Physical Properties | |
| Density | 3.18 g/cm3 |
| Melting Point | 1255℃ |
| Thermal Conductivity | 0.3 Wm-1K-1 at 300K |
| Thermal Expansion | 13.7 x 10-6 /℃ parallel c-axis
8.9 x 10-6 /℃ perpendicular c-axis |
| Knoop Hardness | 415 with 100g indenter (kg/mm2) |
| Specific Heat Capacity | 1003 J/(kg.k) |
| Dielectric Constant | 1.87 at 1MHz parallel c-axis
1.45 at 1MHz perpendicular c-axis |
| Youngs Modulus (E) | 138.5 GPa |
| Shear Modulus (G) | 54.66 GPa |
| Bulk Modulus (K) | 101.32 GPa |
| Elastic Coefficient | C11=164; C12=53; C44=33.7
C13=63; C66=96 |
| Apparent Elastic Limit | 49.6 MPa (7200 psi) |
| Poisson Ratio | 0.276 |
| Chemical Properties | |
| Solubility | 0.0002 g/ 100g water at 20℃ |
| Molecular Weight | 62.32 |
| Structure | Tetragonal Crystal |
| Cleavage Plane | (110) |
| No = Ordinary Ray, Ne = Extraordinary Ray | |||||
| µm | No | Ne | µm | No | Ne |
| 0.1198 | 1.6510 | 1.655 | 0.121 | 1.628 | 1.632 |
| 0.140 | 1.5095 | 1.523 | 0.150 | 1.480 | 1.494 |
| 0.170 | 1.448 | 1.462 | 0.180 | 1.439 | 1.453 |
| 0.200 | 1.423 | 1.437 | 0.220 | 1.413 | 1.426 |
| 0.257 | 1.401 | 1.414 | 0.266 | 1.399 | 1.412 |
| 0.300 | 1.393 | 1.405 | 0.330 | 1.389 | 1.402 |
| 0.350 | 1.387 | 1.400 | 0.355 | 1.386 | 1.399 |
| 0.546 | 1.379 | 1.390 | 0.700 | 1.376 | 1.388 |
| 1.512 | 1.370 | 1.382 | 2.000 | 1.368 | 1.379 |
| 3.030 | 1.360 | 1.370 | 3.571 | 1.354 | 1.364 |
| 4.546 | 1.341 | 1.350 | 5.000 | 1.334 | 1.343 |
| 6.060 | 1.314 | 1.321 | |||
| Specification | Typical Level | High precision |
| Sizes | 2mm-150mm | 2mm-200mm |
| Diameter tolerance | +/-0.1mm | +/-0.05mm |
| Thickness tolerance | +/-0.1mm | +/-0.05mm |
| Surface quality, scr/dig | 60/20 | 10/5 |
| Surface flatness(lambda) | L/2 | L/10 |
| Parallelism | 3 arc min | 10 arc sec |
| Clear Aperture | 80% | 90% |
| Chamfer | 0.25mm at 45 deg | 0.15mm at 45 deg |
| Coating | As requested | As requested |
Lae koste plano /sferiese /asferiese /silindriese MgF2 optika word gebruik vir optiese elemente in die infrarooi waar uiterste robuustheid en duursaamheid benodig word. Die enkele MgF2-kristal vertoon effense dubbelwisseling deur sy bruikbare transmissiereeks en die birefrendece in die infrarooi kan nuttig wees.
Transmitte goed in die VUV streek by die waterstof Lyman-alfa lyn (121nm) en verder. Dit word ook gebruik vir die meeste UV-optika en is uitstekend vir excimer laser toepassing. Honor Optics is die professionele VGV, UV en IR graad MgF2 optiese vervaardiger, welkom om die prys van groothandel MgF2 optika te raadpleeg. Welkom almal om groot grootte laser graad MgF2 optika te koop.
Lae koste plano /sferiese /asferiese /silindriese MgF2 optika word gebruik vir optiese elemente in die infrarooi waar uiterste robuustheid en duursaamheid benodig word. Die enkele MgF2-kristal vertoon effense dubbelwisseling deur sy bruikbare transmissiereeks en die birefrendece in die infrarooi kan nuttig wees.
Honor Optics is die professionele vervaardiger van MgF2 (Magnesium Fluoried) met ROHS beskerming van die omgewing. Honor Optics kan bied:
UVU-eksimervlak, UV en IR-vlak MgF2 (Magnesium Fluoried) optiese komponente met verskillende vorms, soos staaf, vierkant, stap, wig, prisma, bolvormig, silindries en so aan.
Mono- of poli kristal, maksimum grootte is ongeveer 200mm
Oriëntasie: <001>, <100>, <110>, <111>, <210>